里氏硬度计测试范围(表一)
材料 | 硬度制 | 冲击装置 | |||||
D/DC | D+15 | C | G | E | DL | ||
Steel and cast steel 钢和铸钢 | HRC | 17.9~68.5 | 19.3~67.9 | 20.0~69.5 | 22.4~70.7 | 20.6~68.2 | |
HRB | 59.6~99.6 | 47.7~99.9 | 37.0~99.9 | ||||
HRA | 59.1~85.8 | 61.7~88.0 | |||||
HB | 127~651 | 80~638 | 80~683 | 90~646 | 83~663 | 81~646 | |
HV | 83~976 | 80~937 | 80~996 | 84~1042 | 80~950 | ||
HS | 32.2~99.5 | 33.3~99.3 | 31.8~102.1 | 35.8~102.6 | 30.6~96.8 | ||
Steel锻钢 | HS | 32.2~99.5 | |||||
CWT、ST 合金工具钢 | HRC | 20.4~67.1 | 19.8~68.2 | 20.7~68.2 | 22.6~70.2 | ||
HV | 80~898 | 80~935 | 100~941 | 82~1009 | |||
HRA | 60.7~92.6 | ||||||
HB | 232~625 | ||||||
Stainless steel 不锈钢 | HRB | 46.5~101.7 | |||||
HB | 85~655 | ||||||
HV | 85~802 | ||||||
GC. IRON 灰铸铁 | HRC | ||||||
HB | 93~334 | 92~326 | |||||
HV | |||||||
NC、IRON 球墨铸铁 | HRC | ||||||
HB | 131~387 | 127~364 | |||||
HV | |||||||
C.ALUM 铸铝合金 | HB | 19~164 | 23~210 | 32~168 | |||
HRB | 23.8~84.6 | 22.7~85.0 | 23.8~85.5 | ||||
HV | 83.2~648.2 | ||||||
BRASS 铜锌合金 | HB | 40~173 | |||||
HRB | 13.5~95.3 | ||||||
BRONZE铜锡(铝)合金 | HB | 60~290 | |||||
COPPER纯铜 | HB | 45~315 |
示值误差和示值重复性(表二)
异型冲击装置 | DC(D)/DL | D+15 | C | G | E |
冲击能量 | 11mJ | 11mJ | 2.7mJ | 90mJ | 11mJ |
冲击体质量 | 5.5g/7.2g | 7.8g | 3.0g | 20.0g | 5.5g |
球头硬度 | 1600HV | 1600HV | 1600HV | 1600HV | 5000HV |
球头直径 | 3mm | 3mm | 3mm | 5mm | 3mm |
球头材料 | 碳化钨 | 碳化钨 | 碳化钨 | 碳化钨 | 金刚石 |
冲击装置直径 | 20mm | 20mm | 20mm | 30mm | 20mm |
冲击装置长度 | 75mm | 162mm | 141mm | 254mm | 155mm |
冲击装置重量 | 50g | 80g | 75g | 250g | 80g |
试件硬度 | 940HV | 940HV | 1000HV | 650HB | 1200HV |
试件表面平均粗糙度Ra | 1.6μm | 1.6μm | 0.4μm | 6.3μm | 1.6μm |
试件最小重量 | >5kg | >5kg | >1.5kg | >15kg | >5kg |
可直接测量需稳定支撑 | 2~5kg | 2~5kg | 0.5~1.5kg | 5~15kg | 2~5kg |
欧谱硬度计需密实耦合 | 0.05~2kg | 0.05~2kg | 0.02~0.5kg | 0.5~5kg | 0.05~2kg |
试件最小厚度密实耦合 | 5mm | 5mm | 1mm | 10mm | 5mm |
硬化层最小深度 | ≥0.8mm | ≥0.8mm | ≥0.2mm | ≥1.2mm | ≥0.8mm |
硬度 | 压痕直径 | 0.54mm | 0.54mm | 0.38mm | 1.03mm | 0.54mm | ||||
压痕深度 | 24μm | 24μm | 12μm | 53μm | 24μm | |||||
硬度 600HV时 | 压痕直径 | 0.54mm | 0.54mm | 0.32mm | 0.90mm | 0.54mm | ||||
压痕深度 | 17μm | 17μm | 8μm | 41μm | 17μm | |||||
硬度 800HV时 | 压痕直径 | 0.35mm | 0.35mm | 0.35mm | ---- | 0.35mm | ||||
压痕深度 | 10μm | 10μm | 7μm | 10μm | ||||||
沧州欧谱冲击装置 适用范围 | DC型测量孔或园柱筒内; DL型测量细长窄槽或孔;D型用于常规测量 | D+15型接触面细小,加长,适宜测量沟槽或凹入的表面 | C型冲击力小,对被测表面损伤很小,不破坏硬化层, 适合测量小轻薄部件及表面硬化层。 | G型 测量大厚重及表面较粗糙的铸锻件 | E型 测量硬度*材料 |